Liaoning Epoxy Zinc Rich Primer Port Machinery Coating Special Primer Bridge Steel Structure Anti corrosion Coating

Description :

　　The zinc content in the epoxy zinc rich primer film is relatively high, which has cathodic protection effect, good adhesion, and excellent water resistance and rust prevention performance. It also has the characteristics of fast drying of paint film and oil resistance, and can be matched with most anti rust paints and topcoats. The thickness of the paint film should be controlled at around 20 microns without affecting the welding performance. This paint can be used as a maintenance primer for steel plates in various parts of shipbuilding and bridges after shot blasting treatment, and as an anti-corrosion coating for steel structure surfaces.

　　Color: Zinc Grey

　　Flash point: about 27 ℃

　　Basic parameters: drying time (25 ℃, relative humidity 65%), surface drying for 0.5 hours, actual drying for 24 hours, complete curing for 7 days

　　Painting matching and construction:

　　1. Before painting, first mix and stir the two components A and B of the paint according to the specified ratio, and let them mature for half an hour before painting construction can begin.

　　Paint component A: Component B: 7:1, with a shelf life of 8 hours at 25 ℃ after preparation.

　　2. The paint can be applied using methods such as brushing, rolling, and high-pressure airless spraying.

　　3. Usage parameters: Approximately 80 grams per square meter as maintenance primer, with a dry film thickness of 20 microns. As an anti rust paint, it weighs about 270 grams per square meter and has a dry film thickness of 70 microns.

　　4. Diluent: Epoxy diluent.

　　5. Metal surface treatment: In order to protect metal objects, the steel surface needs to be treated with shot blasting or sandblasting methods to remove oxide scale, rust, oil stains, etc., and can only be coated after reaching a rust removal level of Sa2.5.

　　6. Rear supporting coatings: epoxy mica iron thick paste primer, epoxy asphalt series coating, chlorinated rubber coating.

　　7. The curing reaction is slow when the construction environment is below 10 ℃.

　　Packaging specifications: 25kg/barrel of epoxy zinc rich primer slurry (component A), 2.5kg/barrel of curing agent (component B).

　　Storage period: 1 year

AfterSalesService :

• Epoxy zinc rich primer with customizable zinc content