Two component epoxy zinc rich primer for grid structure, epoxy zinc rich primer for iron tower spraying

Description :

　　Epoxy zinc rich primer zinc content can be customized to manufacturers with zinc content of 30 zinc content and 60 zinc content. Epoxy resin curing agent manufacturer

　　1. Inorganic zinc rich primer anti-corrosion inorganic zinc rich primer

　　Using water as a solvent, non-toxic, pollution-free, fast drying, and good flexibility.

　　2. The coating surface can be matched with various anti-corrosion coatings to meet the needs of various long-term heavy-duty anti-corrosion projects.

　　3. Excellent resistance to organic solvents, and the coating has excellent electrochemical corrosion resistance.

　　4. Water based inorganic zinc rich primer can continuously withstand high temperatures up to 400-500 ℃.

　　5. Low resistivity, anti-static, radiation resistant, UV resistant, salt spray resistant, aging resistant, with long-lasting anti-corrosion effect.

　　3、 Application of water-based inorganic zinc rich primer: Used for oil tanks, oil tanks, cargo holds, transmission towers, marine steel structure bridges and large steel roof trusses with harsh environmental conditions, chimneys, offshore platforms, chemical equipment, etc.

　　4、 Technical indicators:

　　project indicators

　　Paint film color and appearance: gray, matte

　　Adhesion, Level 1

　　Impact resistance strength, kg.cm， Not less than 50

　　Hardness (pencil method) not less than 1H

　　Adhesion, grade, not greater than 2

　　drying time

　　h， Not greater than stem 1

　　Practical Action 2

　　Drying (80 ± 2 ℃)--

　　Salt spray resistance: Surface intact after 2500 hours (dry film of 100 microns)

　　Surface integrity after 1500 hours of aging resistance test

　　Surface integrity after 1500 hours of moisture and heat resistance

　　Flexibility, mm1

AfterSalesService :

• Network frame two-component epoxy zinc rich primer