Sihai brand acrylic modified silicone resin high-temperature resistant coating base material manufacturer
Category:
chemical industry/synthetic resin/Organic silicone resin
Model:
Brand:
all corners of the world
brand:
all corners of the world
grade:
SH-024-5
content:
50-60
purpose:
This product is widely used as a high-temperature and anti-corrosion coating (200-400 ℃), insulation coating, weather resistant coating, etc. It can be fully cured at room temperature with two components. Compared to 023-7, 023-4 has better corrosion resistance but slightly lower high temperature resistance.
CAS:
67763-03-5
viscosity:
10-65
solid content:
fifty
color:
Colorless Transparent Liquid
appearance:
Colorless Transparent Liquid
Processing Technology:
Thermoplastic silicone resin
Place of Origin:
Zaoyang, Hubei
manufacturer:
Hubei Longsheng Sihai
Retail Price
Negotiable
重量
kg
- Product Description
-
brand all corners of the world
grade SH-024-5
content 50-60
purpose This product is widely used as a high-temperature and anti-corrosion coating (200-400 ℃), insulation coating, weather resistant coating, etc. It can be fully cured at room temperature with two components. Compared to 023-7, 023-4 has better corrosion resistance but slightly lower high temperature resistance.
CAS 67763-03-5
viscosity 10-65
solid content fifty
color Colorless Transparent Liquid
appearance Colorless Transparent Liquid
Processing Technology Thermoplastic silicone resin
Place of Origin Zaoyang, Hubei
manufacturer Hubei Longsheng Sihai
Description :
SH-024-5 Acrylic modified silicone resin
1、 Performance and Application
This product is prepared by a special process using silanol hydrolyzed from phenyl and methyl monomers and special acrylic monomers. It combines the advantages of acrylic resin and organosilicon resin, with excellent heat resistance and weather resistance, strong adhesion, and low-temperature curing. Suitable for blending various series of high-temperature resistant coatings, weather resistant coatings, and H-grade silicone insulation paints. Sihai brand acrylic modified silicone resin high-temperature resistant coating base material manufacturer
2、 Main technical indicators
project
indicator
Test Method
appearance
Light yellow to light brown liquid, allowed to have
Milky white light, no mechanical impurities
GB1721
Viscosity (Apply -4 cups, 25 ℃, S)
15~40
GB1723
Solid content (150 ℃, 2h),%
50±1
GB1725
Drying time (200 ℃, h）
≯1.5
GB1728 Heat resistance (250 ℃, 200h)
No bubbles, no cracks
GB1735 3、 Packaging and Storage Transportation
This product is packaged in a 200kg iron drum and stored in a cool and dry place. It should be protected from direct sunlight and avoid contact with acids and alkalis. It should be stored and transported as a dangerous goods.
4、 Construction reference
1. Two component curing at room temperature, used in combination with isocyanate or polyamide curing agents such as Bayer 3390, N75, HDI, etc., with a dosage of 15-25% of the total resin.
2. High temperature baking curing, fully cured after heating to 180 ℃ for one hour. It can also be combined with amino resin to shorten the curing time.
3. The dilution solvent used in this product must not contain water, acid, alkali, amine compounds, sulfur-containing compounds, pyridine and its impurities, otherwise it will affect the adhesion, dryness and other properties of the resin paint film.
4. This product contains volatile flammable and explosive solvents. During the processing, attention should be paid to strengthening on-site ventilation, fire prevention, and strictly cutting off fire sources. Operators should pay attention to labor protection.
5. The equipment and tools used in the processing of this product must be clean. Strictly prevent the mixing of dust, foreign objects, and water.
AfterSalesService :
Key words:- Acrylic modified silicone resin