LCP DuPont 6130LX-WT010 in stock
Category:
Rubber and plastic/engineering plastic/LCP
Model:
Brand:
DuPont, USA
Retail Price
67.90USD
重量
kg
- Product Description
-
Description :
LCP DuPont 6130LX-WT010 in stock
LCP has many excellent characteristics and can be used as an engineering plastic for connectors in electronic devices such as mobile phones and computers, as well as for headlight housings in automobiles; As a fiber, it can be used as a reinforcement material for airbags, tires, and optical fibers; Alloy can be used for corrosion-resistant chemical pumps, automotive brake pads, and high-end audio pickups.
Celanese Zenite® 6130LX BK010 LCP Physical Properties Table
Physical performance rating (metric) rating (imperial) testing method
Specific gravity 1.66 g/cc ASTM 792
Density 1.66 g/cc 0.0600 lb/in3 ISO 1183
Filler content 30% 30%
Linear molding shrinkage rate, Flow 0.0012 cm/ cm@Thickness 2.00 mm 0.0012 in/ in@Thickness 0.0787 in ISO 294-4
Linear molding shrinkage rate, transverse 0.0060 cm/ cm@Thickness 2.00 mm 0.0060 in/ in@Thickness 0.0787 in ISO 294-4
Mechanical performance rating (metric) rating (imperial) testing method
Tensile strength (fracture) 145 MPa 21000 psi ISO 527
Ultimate tensile strength 151 MPa@Temperature 23.0 °C 21900 psi@Temperature 73.4 °F ASTM 638
Elongation (at break) 1.8% 1.8% ISO 527
2.6 %@Temperature 23.0 °C 2.6 %@Temperature 73.4 °F ASTM 638
Tensile modulus 15.0 GPa@Temperature 23.0 °C 2180 ksi@Temperature 73.4 °F ISO 527
Bending strength 197 MPa@Temperature 23.0 °C 28600 psi@Temperature 73.4 °F ASTM 790
two hundred and twenty MPa@Temperature 23.0 °C 31900 psi@Temperature 73.4 °F ISO 178
Bending modulus 12.8 GPa@Temperature 23.0 °C 1860 ksi@Temperature 73.4 °F ISO 178
fourteen point five GPa@Temperature 23.0 °C 2100 ksi@Temperature 73.4 °F ASTM 790
Suspended wall beam notch impact strength 1.07 J/ cm@Temperature 23.0 °C 2.00 ft-lb/ in@Temperature 73.4 °F ASTM 256
Simply supported beam without notch impact strength 4.00 J/ cm2@Temperature 23.0 °C 19.0 ft-lb/ in2@Temperature 73.4 °F ISO 179/1eU
The impact strength of the simply supported beam gap is 2.00 J/ cm2@Temperature 23.0 °C 9.52 ft-lb/ in2@Temperature 73.4 °F ISO 179/1eA