Vacuum evaporation of COC from Japan's Rayon 1060R optical grade high flow
ZEONOR® 1060R Physical Property Table
Basic Information
Characteristics: Low Specific Gravity, high purity, low moisture absorption, moisture resistance, optical performance, good electrical performance, high fluidity, clarity, high
Application: Packaging, Electrical/Electronic Applications, Automotive Applications
Processing methods: blow molding, extrusion, injection molding
Physical performance rating unit testing method
Specific gravity 1.01 g/cm3 ASTM 792
Melting rate (melt flow rate) ISO 1133
230°C/2.16 kg 14 g/10 min ISO 1133
280°C/2.16 kg 60 g/10 min ISO 1133
Water absorption rate (equilibrium)<0.010% ASTM 570
Test method for hardness rating unit system
Rockwell hardness (M grade) 20 ASTM 785
Mechanical performance rating unit testing method
Tensile modulus 2100 MPa ISO 527-2
Tensile stress 53.0 MPa ISO 527-2
Tensile strain (fracture) 60% ISO 527-2
Bending modulus 2100 MPa ISO 178
Bending stress 76.0 MPa ISO 178
Test method for impact performance rating unit system
Suspended wall beam notch impact strength 18 J/m ASTM 256
Test method for thermal performance rating unit system
Hot deformation temperature under load (1.8 MPa, annealed) 99.0 ° C ASTM 648
Glass transition temperature 100 ° C JIS K7121
Linear coefficient of thermal expansion - Flow 7.0E-5 cm/cm/° C ASTM 831
Test method for unit system of rated electrical performance values
Volume resistivity>1.0E+16 ohms · cm IEC 60093
Dielectric strength 70 kV/mm ASTM 149
Dielectric constant (1 MHz) 2.30 IEC 60250
Dissipation factor (1 MHz) 2.0E-4 IEC 60250