High impact and high lubrication LCP 6140L, DuPont 40% fiberglass reinforced, excellent thermal deformation temperature
Category:
Rubber and plastic/engineering plastic/LCP
Model:
Brand:
DuPont, USA
Retail Price
71.50USD
重量
kg
- Product Description
-
Description :
LCP 6140L DuPont, USA
Zenite® 6140L is a 40% glass fiber reinforced and lubricated liquid crystal polymer used for injection molding. It has excellent impact resistance and outstanding thermal deformation temperature. High impact resistance; High lubrication
6140L Physical Properties Table
Basic Information
Yellow card number E344082-100831266
Filler/reinforcement material glass fiber reinforcement material, 40% filler by weight
Additive lubricant
Characteristic impact resistance, good
lubrication
RoHS Compliance Contact Manufacturers
Formal particle
Processing method: Injection molding
Physical performance rating unit testing method
Density 1.71 g/cm3 ISO 1183
Shrinkage rate ISO 294-4
Vertical flow direction 0.50% ISO 294-4
Flow direction 0.050% ISO 294-4
Mechanical performance rating unit testing method
Tensile modulus 17000 MPa ISO 527-2/1A/1
Tensile stress (fracture) 130 MPa ISO 527-2/1A/5
Tensile strain (fracture) 1.1% ISO 527-2/1A/5
Bending modulus (23 ° C) 16500 MPa ISO 178
Bending stress (23 ° C) 190 MPa ISO 178
Test method for impact performance rating unit system
Impact strength of simply supported beam with notch ISO 179/1eA
-30°C 15 kJ/m2 ISO 179/1eA
23°C 15 kJ/m2 ISO 179/1eA
Simply supported beam without notch impact strength ISO 179/1eU
-30°C 20 kJ/m2 ISO 179/1eU
23°C 23 kJ/m2 ISO 179/1eU
Suspended wall beam notch impact strength (23 ° C) 12 kJ/m2 ISO 180/1A
Test method for thermal performance rating unit system
Hot deformation temperature (1.8 MPa, unannealed) 280 ° C ISO 75-2/A
Melting temperature 1 335 ° C ISO 11357-3
Linear coefficient of thermal expansion ISO 11359-2
Flow 4.0E-6 cm/cm/° C ISO 11359-2
Horizontal 6.4E-5 cm/cm/° C ISO 11359-2
Test method for unit system of rated electrical performance values
Surface resistivity>1.0E+15 ohms IEC 60093
Volume resistivity>1.0E+15 ohms · cm IEC 60093
Dielectric strength 45 kV/mm IEC 60243-1
Leakage Trace Index 175 V IEC 60112
Test method for flammability rating unit system
UL flame retardant rating UL 94
0.400 mm V-0 UL 94
1.50 mm V-0 UL 94
Injection rated value unit system
Drying temperature 150 ° C
Drying time 3.0 hours
Suggested maximum moisture content of 0.010%
Processing (melt) temperature 350 to 360 ° C
Mold temperature ranging from 40.0 to 150 ° C
AfterSalesService :
Key words:- High impact resistance and high lubrication