High temperature resistant LCP 7145L with excellent impact lubrication from DuPont in the United States
Category:
Rubber and plastic/engineering plastic/LCP
Model:
Brand:
DuPont, USA
Retail Price
60.00USD
重量
kg
- Product Description
-
Description :
LCP 7145L DuPont, USA
High temperature resistance; V-0; lubricity; Good impact performance;
7145L Physical Property Table
Basic performance rating unit testing method
Density 1740 Kg/m ISO 1183
Mechanical performance rating unit testing method
Fracture strain (4.0mm, 23 ℃ (73 ℉)) 0.9% ISO 527-1,2
Fracture stress (4.0mm, 23 ℃ (73 ℉)) 120 MPa ISO 527-1,2
Bending strength (23 ℃ (73 ℉)) 180 MPa ISO 178
Tensile modulus (23 ℃) 22000 MPa ISO 527-1,2
Bending modulus (23 ℃ (73 ℉)) 24000 MPa ISO 178
Dielectric strength (23 ℃ (73 ℉)) 21 Kv/mm ASTM -149
Fracture strain (1.0mm, 23 ℃ (73 ℉)) 0.6% ISO 527-1,2
IZOD notch impact strength 8.5 KJ/m ISO 180/1A
Fracture strain (2.0mm, 23 ℃ (73 ℉)) 0.9% ISO 527-1,2
IZOD Impact Strength ASTM -256
(1.6mm(0.062in)) 90 J/m
(0.79mm(0.031in)) 190
Charpy notch free impact strength (23 ℃ (73 ℉)) 18 KJ/m ISO 179 LeU
Tensile modulus (23 ℃ (73 ℉)) 18000 MPa ISO 527-1,2
Bending modulus (23 ℃ (73 ℉)) 16300 MPa ISO 178
Fracture stress (1.0mm, 23 ℃ (73 ℉)) 140 MPa ISO 527-1,2
Bending strength ISO 178
(23℃(73℉)) 210 MPa
(23℃(73℉)) 230 MPa
IZOD impact strength (3.2mm (0.126in)) 60 J/m ASTM -256
Tensile modulus (23 ℃) 20500 MPa ISO 527-1,2
CHARPY notch impact strength (23 ℃ (73 ℉)) 10 KJ/m ISO 179 LeA
Bending modulus (23 ℃ (73 ℉)) 20500 MPa ISO 178
Fracture stress (2.0mm, 23 ℃ (73 ℉)) 130 MPa ISO 527-1,2
Unit testing method for rated electrical performance values
Loss factor (3.2mm (0.125in), 23 ℃ (73 ℉)) 0.025 ASTM -150
Dielectric strength ASTM -149
(3.2mm(0.125in)) 19 Kv/mm
(23℃(73℉)) 27 Kv/mm
Loss factor (1 × 10Hz) 130 IEC 60250
Dielectric constant (1 × 10Hz) 4.8 IEC 60250
Dielectric constant (3.2mm (0.125in), 23 ℃ (73 ℉)) 4.3 ASTM -150
Loss factor (3.2mm (0.125in), 23 ℃ (73 ℉)) 0.014 ASTM -150
Dielectric strength (0.79mm (0.031in)) 25 Kv/mm ASTM -149
Dielectric constant ASTM -150
(3.2mm(0.125in), 23℃(73℉)) 4.6
(3.2mm(0.125in), 23℃(73℉)) 4.3
Loss factor (3.2mm (0.125in), 23 ℃ (73 ℉)) 0.013 ASTM -150
Dielectric strength (23 ℃ (73 ℉)) 34 Kv/mm ASTM -149
Volume resistivity>1 × 10 Ohm cm IEC 60093
Surface resistivity>1 × 10 Ohm IEC 60093
Dielectric strength (1.6mm (0.062in)) 24 Kv/mm ASTM -149
Unit testing method for thermal performance rating
Drying temperature 130 ℃
Molding temperature range 30-160 ℃
Industrial moisture content<0.01%
Chain breaking temperature range 360-370 ℃