- Product Description
-
Description :
PC AL2447 Shanghai Covestro
MVR (300 ° C/1.2 kg) 19cm3/10 minutes; Automotive lighting; Low viscosity UV stability; Easy to release; Injection molding - melt temperature 280-320 ° C; provides transparent colors and various signal colors; Headlight lens for car headlights
Containing release agent; HB; V-2; Low viscosity; Weather resistant and UV resistant;
camera lens; Applications in the automotive field; Lighting applications;
AL2447 Physical Property Table
Basic Information
Yellow card number E41613-233136
Additive UV stabilizer
Characteristic low viscosity
Good demolding performance
Usage: Lighting Applications
lens
Applications in the automotive field
RoHS Compliance RoHS Compliance
Available colors for appearance
Clear/Transparent
Processing method: Injection molding
Multi point data Specific Volume vs Temperature (ISO 11403-2)
Viscosity vs. Shear Rate (ISO 11403-2)
Physical performance rating unit testing method
Density (23 ° C) 1.20 g/cm3 ISO 1183
Apparent density 1 0.66 g/cm3 ISO 60
Melt flow rate (melt flow rate) (300 ° C/1.2 kg) 20 g/10 min ISO 1133
Dissolved Volume Flow Rate (MVR) (300 ° C/1.2 kg) 19.0 cm3/10 min ISO 1133
shrinkage rate
Vertical flow direction 0.50 to 0.70% ISO 2577
Flow direction 0.50 to 0.70% ISO 2577
Vertical flow direction: 2.00 mm 2 0.70% ISO 294-4
Flow direction: 2.00 mm 3 0.65% ISO 294-4
Water absorption rate ISO 62
Saturation, 23 ° C 0.30% ISO 62
Balance, 23 ° C, 50% RH 0.12% ISO 62
Test method for hardness rating unit system
Ball compression hardness 115 MPa ISO 2039-1
Mechanical performance rating unit testing method
Tensile modulus (23 ° C) 2400 MPa ISO 527-2/1
tensile stress
Yield, 23 ° C 66.0 MPa ISO 527-2/50
Fracture, 23 ° C 70.0 MPa ISO 527-2/5
Fracture, 23 ° C 65.0 MPa ISO 527-2/50
tensile strain
Yield, 23 ° C 6.0% ISO 527-2/50
Fracture, 23 ° C 130% ISO 527-2/5
Fracture, 23 ° C 120% ISO 527-2/50
Nominal tensile fracture strain (23 ° C)>; 50 % ISO 527-2/50
Tensile creep modulus ISO 899-1
1 hr 2200 MPa ISO 899-1
1000 hr 1900 MPa ISO 899-1
Bending modulus 4 (23 ° C) 2350 MPa ISO 178
Bending stress 5 ISO 178
3.5% strain, 23 ° C 74.0 MPa ISO 178
23°C 98.0 MPa ISO 178
Flexural Strain at Flexural Strength (23°C) 6 7.0 % ISO 178
Test Method for Film Rating Unit System
Gas Permeation ISO 2556
Carbon Dioxide : 23°C, 25.4 μm 18900 cm3/m2/bar/24 hr ISO 2556
Carbon Dioxide : 23°C, 100.0 μm 4800 cm3/m2/bar/24 hr ISO 2556
Nitrogen : 23°C, 25.4 μm 630 cm3/m2/bar/24 hr ISO 2556
Nitrogen : 23°C, 100.0 μm 160 cm3/m2/bar/24 hr ISO 2556
Oxygen : 23°C, 25.4 μm 3150 cm3/m2/bar/24 hr ISO 2556
Oxygen : 23°C, 100.0 μm 800 cm3/m2/bar/24 hr ISO 2556
Test method for flammability rating unit system
Flash Ignition Temperature 480 °C ASTM 1929
Self Ignition Temperature 550 °C ASTM 1929
Supplementary Information Rating Test Method
Electrolytical Corrosion (23°C) A1 IEC 60426
ISO Shortname ISO 7391-PC,MLR,(,,)-18-9
Test Method for Film Rating Unit System
Water vapor permeability (23 ° C, 85% RH, 100 μ m) 15 g/m2/24 hr ISO 15106-1
Test method for impact performance rating unit system
Simply supported beam notch impact strength 7 ISO 7391
-30 ° C, complete fracture 14 kJ/m2 ISO 7391
23 ° C, local fracture 65 kJ/m2 ISO 7391
Simply supported beam without gap punching